Abstract Abstract In this investigation, silver coated alumina reinforced aluminum nano-composite matrix is synthesized by the double cold and double hot pressing (DCDH) method for the first time. Aluminum, copper, and nano-nickel are the main elements of the composite matrix. The electro-less coating process was used to prepare nano-nickel powder. The alumina powder was ball milled for 35 hr. In order to improve the contact between the alumina ceramic reinforcement and the aluminum campsite matrix, the Al2O3 was coated with 5 wt. %Ag by the electro-less coating process. Five composites that contain 0, 10, 15, 20, and 25 wt. % (Al2O3-5Ag) were prepared by mixing them for 6 hr. Each composite was cold pressed at 800 MPa and heated in the die at 630 oC, then hot pressed at 600 MPa, and finally ejected from the die. To investigate the chemical composition of the powders and fabricated composites, the X-ray diffraction and EDAX analysis were used. The Archimedes’ method and the scanning electron microscopy (SEM) were used respectively to measure the density and to investigate the microstructure of the fabricated composites. Some of the mechanical and physical properties such as hardness, toughness, wear, relative density, and thermal expansion, were characterized. All the fabricated composites exhibited full density. During the heating process, a reaction was taking place, and new phases, which are AlCu3 and Al3Ni were formed. The microstructure of the fabricated composites shows an excellent distribution of the Cu, nano-Ni, and of the different percentages of the (Al2O3-5Ag). Regardless of the high difference in the melting point of the Al composite matrix and the Al2O3, good adhesion between them was confirmed. 288.8% and 473.8% were enhancements in the hardness as a result of reinforcing pure aluminum with (10Cu, and 10nano-Ni) and a 25 wt. % of (Al2O3-5Ag), respectively, was achieved. In spite of reinforcing (Al-10Cu-10nano-Ni) nano-composite matrix with high percentages of (Al2O3-5Ag), the composites exhibited a good toughness. Because of the high hardness of the Al2O3 phase, the wear rate was dramatically decreased from 4.2mg to 0.88mg at 25 wt. % (Al2O3-Ag). The coefficient of thermal expansion of the composites was getting decreased as the percentage of the (Al2O3-5Ag) increased. |