Abstract
Summary
This study aimed to investigate the effect of dimethyl sulfoxide wet bonding technique, using three different concentrations, in enhancing the dentin wettability by the adhesive and the resin-dentin bond strength durability. DMSO wet bonding technique was compared to ethanol wet bonding technique in its simplified form and the conventional bonding technique.
The two adhesive resins used were, single bond 2 (SB2), a two-step etch and rinse adhesive and single bond universal (SU) which was applied in etch and rinse mode. Two adhesive resins were investigated to clarify which adhesive best matches the pretreatments used providing higher resin-dentin bond durability. Specimens were randomly distributed into five groups according to the pretreatment used; each group was further divided into 2 subgroups according to the adhesive applied. Dentin specimens that remained untreated served as the control group.
The wettability of the adhesive by DMSO vs. ethanol saturated dentin was evaluated through contact angle measurement. Teeth were cut parallel to the occlusal surface to obtain flat dentin slices. A total of 50 slices were obtained, each one measuring 1mm (±1mm) in thickness and checked using a digital caliper. Following the acid etching procedure, dentin pretreatments using (DMSO: 0.004%, 5%, and 50% or ethanol 100%) were applied using a saturated micro-brush and left for 1 min. A micro-pipette (Topette Pipettor, Dragon lab) was adjusted to dispense a 10µl droplet of either SB2 or SU adhesive on the flat dentin surface. For the control group, the adhesive was applied on the dentin slices immediately. A digital microscope (Dino-Lite microscope, India) was used for the measurement of the adhesive contact angles.
For the microtensile bond strength testing, pretreatments were applied in the same manner as in contact angle measurement. Teeth were then bonded using the adhesives used according to their corresponding groups. Specimens were further divided into 2 subgroups; one group was evaluated after 24 h while the other after 6 months of aging. Bonded teeth were stored in distilled water and then sectioned into resin-dentin sticks using a sharp diamond saw (Isomet 4000 linear Precision saw, Buehler) under constant water coolant. A universal testing machine (Instron® norwood, IL, USA) was used for the microtensile bond strength testing. Tensile loads were applied at a cross-head speed of 1mm/min until failure.
The results for the contact angle measurement showed that dentin pretreatment by ethanol or high DMSO concentrations (5% and 50%) significantly decreased the contact angle of SB2 adhesive. Only the DMSO (5% and 50%) showed a significant decrease in SU adhesive contact angle. As for the effect of the pretreatments alone, all provided a decrease in the contact angle when compared to the control group. DMSO 50% showed significantly the lowest contact angle than all other pretreatments except for the 5% concentration.
Concerning the microtensile bond strength test, results for specimens tested after 24 hours showed that the application of ethanol and DMSO 50% significantly increased the bond strength of SB2 over SU. As for specimens tested after 6 months, only DMSO 5% and 50% recorded significantly higher bond strength of SB2 over SU.
When comparing the difference between the pretreatments within each bond, it was noticed that only DMSO 50% showed significantly higher bond strength values with SB2 in the 24 hours group. While in the aged group, DMSO 5% as well as 50% showed significantly higher bond strength with SB2. Results for the SU group in either measurement times showed no difference in bond strength values.
Results of each variable as a main effect; concerning the time of measurement, it was shown that immediately tested specimens have significantly higher bond strength values than the aged ones. As for the adhesive type, SB2 adhesive recorded significantly higher bond strength than SU. Finally, pretreatment with DMSO 50% showed significantly higher bond strength value than any other pretreatment.
الهدف من الدراسة :
تهدف هذه الدراسة المعملية لتقييم أثر معالجة عاج الاسنان بثلاثة تركيزات مختلفة من ثنائي ميثيل السالفوكسيد و الايثانول علي قابلية العاج للبلل و على قوة الربط بين العاج و الراتنج , و ذلك عن طريق قياس :
1. زاوية الاتصال لللاصق الراتنجي.
2. قوة الربط الدقيقة بين الحشو الراتنجي و عاج الاسنان بعد 24 ساعة و بعد 6 أشهر من التخزين في الماء المقطر.
طرق البحث و المواد المستخدمة:
المواد المستخدمة:
1. ثنائي ميثيل السالفوكسيد
2. الايثانول
3. لاصق راتنجي بالتخريش و الشطف
4. لاصق راتنجي عالمي
5. تخريش حامضي هلامي
6. حشو راتنج مركب
طرق البحث:
التقسيم :
تم تقسيم العينات الي 5 مجموعات طبقا لنوع المعالجة
المجموعة 1: لا معالجة
المجموعة 2: المعالجة بالايثانول بتركيز 100%
المجموعة 3: المعالجة بثنائي ميثيل السالفوكسيد بتركيز 0,004%
المجموعة 4: المعالجة بثنائي ميثيل السالفوكسيد بتركيز 5%
المجموعة 5: المعالجة بثنائي ميثيل السالفوكسيد بتركيز 50%
ثم تم تقسيم كل مجموعة الى مجموعتان فرعيتان طبقا لنوع اللاصق الراتنجي المستخدم الى
المجموعة الفرعية (أ) : المعالجه بلاصق راتنجي بالتخريش و الشطف
المجموعة الفرعية (ب) : المعالجه ب لاصق راتنجي عالمي
في حالة قياس قوة الربط تم القياس بعد 24 ساعة و 6 اشهر من التخزين في الماء المقطر
الطريقة :
تحضير محلول ثنائي ميثيل السالفوكسيد:
تم تحضير 3 تركيزات مختلفة من محلول ثنائي ميثيل السالفوكسيد المخفف بالماء في معامل الكيمياء بجامعة بدر بالقاهرة
قياس زاوية الاتصال:
تحضير عينات زاوية الاتصال:
تم جمع 25 ضرس سليم و غير مصاب بالتسويس تم قلعه حديثا و حفظ في ماده ماء مقطر و استخدامهم خلال 6 أشهر على الاكثر من تاريخ القلع.
تم قطع كل ضرس بقرص ماسي حاد بطيئ السرعة و تحت تبريد مائي غزير لازاله مينا الضروس من سطحها و الحصول على سطح مستوي من العاج. ثم تم قطع الضروس بقطع اخر مشابه بعد سمك 1 ملليمتر للحصول على اقراص من العاج سمكها 1 ملليمتر و تم الحصول على 50 قرص بهذة الطريقة.
تم تشطيب كل قرص باستخدام ورق قاشط لمدة 60 ثانية لازالة اي بقايا من القطع و للحصول على سطح املس للاقراص.
تم تخريش سطح الاقراص بالحامض الهلامي لمدة 15 ثانية ثم شطفها بالماء و تجفيفها بالهواء. ثم تم معالجة الاسطح المخرشة بالمعالجات الخمسة المذكورة سابقا.
بعد المعالجة تم استعمال قطارة دقيقة لانزال قطرة واحدة من كل نوع من اللاصق الراتنجي (لاصق راتنجي بالتخريش و الشطف, و لاصق راتنجي عالمي) على كل القرص. ثم قياس زاوية اللصق باستخدام ميكروسكوب اليكتروني.
اختبار قوة الربط:
تم جمع 20 ضرس سليم و غير مصاب بالتسويس تم قلعه حديثا و حفظ في ماده ماء مقطر و استخدامهم خلال 6 أشهر على الاكثر من تاريخ القلع.
تم استخدام قالب اسطواني من التفلون ( سمكه 15 ملليمتر و ارتفاعه 40 ملليمتر ) للحصول على كتل اسطوانيه من الراتنج. ثم تم تثبيت الاسنان في تلك الكتل باستخدام لاصق راتنجي و تحميلها على جهاز التقطيع بالقرص الماسي بطئ السرعة.
تم ازالة مينا الضروس للحصول على سطح مستوي من العاج, ثم تم تشطيب سطح العاج بورق الشطف للحصول على سطح خشن مشابه لسطح الاسنان بعد القطع في الحالات السريرية.
ثم تم توزيع الاسنان بطريقة عشوائية لمجموعات